PTW-582 WATER REDUCIBLE EPOXY PRIMER
Part Number: PTW-582
Military Specification: MIL-PRF -85582D. BMS 10-11Y TY I, CL A, GR E. -- NAVY QPD (QUALIFIED PRODUCTS DATABASE)
PTW-582 Water Reducible Epoxy Primer is chemical and solvent resistant. It is especially recommended to inhibit corrosion of aluminum and other plated or unplated metallic surfaces. PTI’s Water Reducible Epoxy Primer is recommended for all PTI topcoats to provide maximum adhesion and corrosion protection.
PTW-582 Water Reducible Epoxy Primer is chemical and solvent resistant. It is a TUF/FILM epoxy primer that conforms to MIL-PRF -85582D. BMS 10-11Y TY I, CL A, GR E. It is especially recommended to inhibit corrosion of aluminum and other plated or unplated metallic surfaces. PTI’sWater Reducible Epoxy Primer is recommended for all PTI topcoats to provide maximum adhesion and corrosion protection.
LIGHT GREEN, DARK GREEN AND BMS COLORS
Shelf life is only applicable for materials stored in unopened and undamaged original factory filled containers.1 year when stored at 50⁰-85⁰ F.Shake component A in a paint shaker for 5 – 10 minutes for optimal results.
Admix by volume:
For a Viscosity of 22 seconds in a #2 Zahn:
For a Viscosity of 18 seconds in a #2 Zahn:
Add the Catalyst into the Base.
Admixed material should be allowed a 45-minute induction time for best application results.
Reduce: Use distilled water to thin or reduce the primer according to the instructions above. DO NOT OVER-THIN THIS MATERIAL.
This product can be applied by brushing, rolling or using conventional air or HVLP spray equipment.
NOTE: Application of PTI products requires the use of all OSHA approved safety equipment, including proper ventilation. Additionally, PTI products require the recommended temperature/humidity conditions and film thickness ranges for optimal performance. The material, hangar, and aircraft skin temperatures should be no lower than 75⁰ F / 25⁰ C before, during and after application.
Dry times are based on the dry film thickness between 0.6 - 0.9 mils (25-50 microns).Air Cure:Tack Free 60 minutes maximumDry Hard 6 hours maximumForce Cure:Tack Free ½ hour @150FDry Hard 1 hour @ 150F Always bring the coating to the “tack free” stage before top coating.
If using PTI additives to adjust the dry and cure times of the coating, please refer to those Product DataSheets for specific instructions for admixing the material.